  • Extrusion Grade Thermoplastic Elastomers (TPEs)

Extrusion Grade Thermoplastic Elastomers (TPEs)

Extrusion is a process used to create objects of a fixed cross-sectional profile. A material is pushed through a die of the desired cross-section. The two main advantages of this process over other manufacturing processes are its ability to create very complex cross-sections, and to work materials that are brittle, because the material only encounters compressive and shear stresses. It also forms parts with an excellent surface finish.

Phon Tech has developed several PHOENIX™ Extrusion Grade Thermoplastic Elastomers (TPEs) that are suitable for extrusion profile, tube, film and sheet. The material has low MFI and very consistent quality for continual process of extrusion. Typically, the MFI of TPEs should be less than 3g/10min.

PHOENIX™ Extrusion Grade Thermoplastic Elastomers (TPEs) can be co-extruded with PP and PE, which creates an excellent combination of hard and soft material. Soft and hard TPEs combination can also be done by PHOENIX™ Extrusion Grade Thermoplastic Elastomers (TPEs).
Product Series
PHOENIX™ Translucent TPE 04 Series (Shore 30A ~ 80A)
SEBS based. High resilience grade with lowest melt flow index (MFI). For extrusion and blow molding. RoHS compliant. Conform to FDA, ISO 10993-5 & ISO 10993-10. Suitable for medical tube, extrusion profile, blown film, sheet

PHOENIX™ Black TPE 07 Series (Shore 15A ~ 95A)
SEBS based. Common grade for window profile and tube

PHOENIX™ Alloy TPE 16 Series (Shore 45A ~ 95A)
TPV+SEBS based. Higher heat resistance and good surface finish.
Suitable for window seal, extrusion profile, wire and cable sheath
Features
Smooth and silky surface
Non-sticky
Excellent tensile strength
Excellent resilience
Stable melt flow
Applications
tube, profiles, sheets, film, band, wire and cable sheath, etc.
Safety/Quality Approvals
FDA CFR 21 177.2600, RoHS, EN71, REACH SVHC, PAHS & phthalate, Formaldehyde, Dimethyl Fumarate, Nonylphenol, ISO 10993
ITEM Color Hardness Specific Gravity Tensile Strength 100% Tensile Modulus Elongation at Break Tear Strength
    ASTM D2240 ASTM D792 ASTM D412 ASTM D412 ASTM D412 ASTM D624 Die C
    Shore A/D g/cm3 psi psi % lbs/in
04402 Translucent 40±3 A 0.87±0.03 642.7 122.5 690.4 103.6
04501 Translucent 55±3 A 0.88±0.03 1302.6 211.8 1120.7 183.3
04551 Translucent 55±3 A 0.88±0.03 901.7 193 768.4 168
04601 Translucent 60±3 A 0.88±0.03 1150.2 270.4 786.8 224
04651 Translucent 65±3 A 0.89±0.03 1328 291.5 1051.9 220.2
04658 Translucent 65±3 A 0.90±0.03 935.9 281.5 883.9 197.7
04751 Translucent 75±3 A 0.88±0.03 1335.4 378.6 889.6 220.8
ITEM Color Hardness Specific Gravity Tensile Strength 100% Tensile Modulus Elongation at Break Tear Strength
    ASTM D2240 ASTM D792 ASTM D412 ASTM D412 ASTM D412 ASTM D624 Die C
    Shore A g/cm3 psi psi % lbs/in
07606 Black 60±3 A 0.97±0.03 1225.1 223.6 980.4 163.3
07652 Black 70±3 A 1.04±0.03 1134.9 327.2 863.4 185.8
ITEM Color Hardness Specific Gravity Tensile Strength 100% Tensile Modulus Elongation at Break Tear Strength
    ASTM D2240 ASTM D792 ASTM D412 ASTM D412 ASTM D412 ASTM D624 Die C
    Shore A g/cm3 psi psi % lbs/in
16651 Black 70±3 A 1.03±0.03 1301.2 292.3 711.4 196.2
16901 Alloy 90±3 A 1.01±0.03 2437.9 981.9 740.5 445.1